Invigorate® bio-based polymer proves its worth at NCAT, passing tests with three stars.
Producers and asphalt contractors looking to reduce their carbon footprint and meet Environmental Social and Governance (ESG) targets have another proven option at their disposal. The makers of Invigorate, a bio-based rejuvenator that delivers improvements to the molecular makeup of RAP, have successfully completed the first three-year test cycle of their bio-derived polymer at the National Center for Asphalt Technology’s (NCAT) Test Track at Auburn University.
Invigorate Plus additive is a new generation of polymer asphalt additive, designed for high-traffic and heavy-load applications such as interstates and highways. “It consists of one part of our rejuvenator (Invigorate) and one part bio-derived polymer,” explains Austin Hohmann, product manager for Colorbiotics, Ames, Iowa. “It is a hyperbranched polymer that helps to interconnect and extend the SBS (styrene butadiene styrene) domains within asphalt.”
According to Nam Tran, associate director at NCAT, this is the first biobased polymer of its kind undergoing lab and track testing at NCAT. “We have tested some rubber-based polymers, but polymers are typically derived from petroleum. The purpose of the polymer is to improve the rutting and cracking resistance of the binder.”
Just by their nature, plants absorb CO2 and therefore reduce levels in the atmosphere. Using bio-based materials benefits the environment and sustainability efforts. “Polymers made from plants and trees can be considered carbon negative, possibly offering carbon credits,” adds Tran. Petroleum-based polymers are CO2 positive.
Further environmental benefits are reaped along the production chain of bio-based polymers. “On average, it takes two pounds of oil to make one pound of polymer,” offers Hohmann. “By contrast, it takes just under one pound of bio-based oil to make one pound of polymer.” Test results so far also indicate that the mix design may be optimized to increase the amount of RAP used to make the asphalt mix.
Sustainability is only half of the equation. Regardless of the potential environmental benefits, the bio-based polymer must perform as well as petroleum-based binders in the lab and field to offer true benefits for the industry. For that, Colorbiotics worked with NCAT to test the bio-based performance-graded binder against a standard control mix to analyze and compare performance. More than a third of the way through its second three-year cycle, “both sections are performing well at this point,” comments Jason Nelson, NCAT Test Track manager.”
Passing grade
NCAT designed the experiment to evaluate the impact of the new biopolymer on asphalt binder, plant-produced mix and field performance on the NCAT Test Track. Invigorate Plus additive includes bio-based oil to improve the resistance of asphalt binders to oxidative aging. It was blended at an asphalt terminal and delivered to East Alabama Paving, who produced the mix paved at the test track.
The difference between the two new surface mixes tested by NCAT showed only in the type of virgin asphalt binders. Test Track Section W10 was paved with mix using the asphalt binder modified with the Invigorate Plus additive biopolymer, while the control section E5A included the binder modified with the traditional petroleum based SBS polymer. “We produced a mix with the biopolymer that matched the SBS polymer control mix to get an apples-to-apples comparison,” offers Buzz Powell, associate director at NCAT and research professor at Auburn University.
Aggregate gradation for the surface mix included a 12.5-millimeter (0.50 inch) nominal aggregate size, and 20% RAP was introduced at a 12.5-millimeter (0.50 inch) size with 5.5% binder and granite aggregate plus a local sand. Volumetric design parameters for both included 4% air voids, 5.3% total combined binder content with a 4.9% effective binder, and a 2.5% maximum specific gravity.
Binder analysis was based on test results of both the virgin binders and the extracted plant-produced asphalt mixtures that included RAP. A PG 76-22 SBS modified binder was used for the control for E5A, while the supplied W10 experimental binder mixed at the terminal offered a performance grade of PG 70-16. Reviewing the binder test results, researchers noticed differences in the biopolymer when comparing the test results of the virgin and extracted binders.
The asphalt samples at the plant were mixed at a higher temperature than in the lab, and as a result, the extracted W10 biopolymer binder offered a high-temperature performance grade of 88˚C, like the E5A control mix. Additionally, the low-temperature performance of the extracted E5A binder increased from -22˚C to -16˚C, whereas the extracted W10 binder maintained its low-temperature performance of -16˚C. Therefore, both extracted mixes showed the same performance grading.
Hohmann explains the W10 performance improvement of the extracted binder. “There is a reaction that occurs when mixing plant temperatures that we didn’t anticipate happening. Between tank to pavement, the increase in heat catalyzed a reaction not seen in the lab. We thought the increased heat would extend the Biopolymer but didn’t realize it would help to mature it. Therefore, we can add RAP to the mix and increase the performance grade of the biopolymer binder.”
He also noted the Multiple-Stress Creep-Recovery (MSCR) test improvements from the virgin binder to the extracted binder. While both designs passed flexibility tests for the virgin and extracted binders, the virgin lab results indicated that the E5A control sample may perform better than the experimental in the field. “With RAP introduced to the mix, the control sample’s performance lowered, while the Invigorate Plus additve Section W10 sample showed improvement to better than that of the control, which could indicate a better resistance to rutting,” Hohmann added.
A series of standard mixture performance tests were also performed on the samples. These included Dynamic Modulus, Hamburg Wheel Tracking, Illinois Flexibility Test (I-FIT), Energy Ratio, Indirect Tensile Asphalt Cracking (IDEAL-CT), High Temperature Indirect Tensile (HT-IDT), Cantabro Percentage Loss, and Disc Shaped Compaction Tension (DCT) tests. All results showed similar or only minor statistical performance differences between the control and experimental mixtures with no sample failing the acceptable standards.
Excelling in the field
Based on the lab results, Tran noted, “We expected both mixtures to perform very well at the Test Track, and we had no surprises.”
Nelson added, “We are now into 13 million equivalent single axle loads (ESALs) with less cracking noticed in the experimental Section W10.”
Both E5A and W10 surface mixes were paved at the NCAT Test Track in 2018 with the plan of conducting two three-year testing cycles. The first cycle finished in 2021 after logging 10 million ESALs, equivalent to 15-20 years of traffic. At this point, both the control SBS-modified polymer and experimental EBS biopolymer sections were evaluated for rutting, cracking, roughness and macrotexture.
Passing the test with minimal rutting, E5A showed only 2.4-millimeters (0.094 inch) of rutting and W10 had 4.7-millimeters (0.185 inch), well below the threshold commonly considered failing of 12.5-millimeters (0.5 inch). “These results are impressive, as you want some level of rutting of the mix. Otherwise, it will be too stiff, which can result in cracking. The experimental biopolymer binder asphalt is a healthy mix,” comments Powell.
Both mixes offered excellent cracking performance as well. The first crack in the control section wasn’t observed until mid-November 2020, and there was no observed cracking in the Invigorate Plus additive surface by the end of the trafficking cycle on February 28, 2021. Additionally, roughness observations during the cycle using the International Roughness Index (IRI) showed similar changes over time for both the control and experimental surfaces, with Section W10 scoring a 102-inches per mile roughness and Section E5A 112-inches per mile.
The final field performance was surface macrotexture. While Section W10 showed a higher macrotexture at the cycle’s beginning, the change for the two sections was virtually identical at the end.
The second 10 million EASLs cycle is scheduled for completion in 2024. Both Powell and Hohmann offer some thoughts about the Invigorate Plus additive W10 test results and the potential for optimizing the design. “As mentioned, the original goal of W10 design was to match the control mix with 20% RAP added. These test results indicate that the biopolymer produces a healthy mix that could be optimized for RAP content,” says Powell.
Hohmann agrees and adds, “A producer reaps significant ROI benefits at RAP content of more than 25%, as this saves on virgin binder and aggregate. These results give us confidence that we can achieve this with Invigorate Plus additive while offering cost, performance and sustainability advantages for the producer.”